Paulownia Vs. Balsa
 

"Balsa has been incorrectly considered to have the highest strength to weight ratios of any wood in the world.
Paulownia has been thoroughly tested and found to have a higher strength to weight ratio than Balsa!
Auburn University tested the strength of 18 lb p/cubic ft. Paulownia against Balsa, with an average weight of 10 lbs p/cubic foot."
Paulownia Trees: Fast Growing Royal Paulownia Tree vs Balsa Comparison

http://www.rcgroups.com/forums/image...es/popcorn.gif

allora siamo a posto, le abbiamo gia' piantate

In effetti...il mio piano di lavoro è in paulownia ed è del tutto simile al balsa. Direi che è leggermente più duro, probabilmente più leggero ma nel senso della venatura mi sembra molto più soggetto a fratture.

Naturalmente le mie impressioni si basano esclusivamente su quell'esemplare e sappiamo bene che anche il basla può variare moltissimo. Il fatto di aver trovato quel piano più duro superficialmente e più leggero di uno analogo in balsa non significa nulla in quanto è possibile selezionare tavole di balsa con caratteristiche analoghe. Mi pare però più significativo il fatto che nonostante la durezza in rapporto al peso sia molto fragile appunto nel senso della venatura. Una tavola in balsa di quello spessore (3cm) e quella durezza non si creperebbe a quella maniera.

Altre informazioni:

"What are the Wood properties of Paulownia?

Unique wood properties such as lightness, strength, woodworking versatility, and stability under rapid changes in moisture have made paulownia highly desirable. These will be primary reasons for future use in domestic markets.

•Lightness—Paulownia is about 2/3 the weight of the lightest commercial wood in the U.S. The specific gravity of paulownia wood ranges from 0.23 to 0.30 (23 to 30 percent of the weight of water). Average cubic foot weight is 16.55 lbs. The bulk weight of lumber averages 1,382 lbs per thousand board feet compared to yellow poplar (tulip poplar), which weighs 2,190 lbs, or white oak, which weighs 3,337 lbs.
•Strength and stability—Although the wood is light, it is extremely strong and will not split even when spikes are driven into it. Unlike other commercial woods, paulownia does not split and crack with rapid drying.
•Easily worked—Another unique quality is the ease with which it can be worked, especially when green. It is suitable for carving, woodworking, model airplane construction, and peeling for veneer. As it dries, it becomes considerably harder, but not as hard as most domestic woods.
•Easily dried—Paulownia will air dry in about 30 days with no warping. This reduces the cost of kiln-drying."

How to Produce and Market Paulownia (University of Maryland; University of Kentucky)
http://extension.umd.edu/publications/pdfs/eb319.pdf

Palownia wood - better than Balsa??? - RC Groups

+++

Evaluation of Physical and Mechanical Properties of Paulownia Wood Core and Fiberglass Surfaces Sandwich Panel

Manufacturing High Performance Wood Composite Panel from Paulownia

Tutto verissimo, tuttavia come dicevo la robustezza di un legno non si misura in senso assoluto. Un legno può essere duro superficialmente ma rompersi facilmente, o ancora essere resistentissimo in una direzione rispetto alla vena e fragilissimo nell'altra. Certo è una validissima alternativa al balsa ma probabilmente, anzi certamente, non la può sostituire del tutto, semplicemente perchè le sue caratteristiche non sono le stesse. Sicuramente può essere migliore per certe applicazioni ma inferiore per altre, come del resto accade con qualsiasi materiale sulla faccia della terra.

Che ne dite di questo?
Jelutong (albero) :)

Capirai, già siamo diventati scemi a capire se si diceva il balsa o la balsa, mò con tutti sti nomi esotici :icon_rofl

Paulownia Vs. Balsa
 

Paulownia,Jelutong,Ferula,Bamboo ecc.
Se tutti vengono comparati al legno di balsa significa una sola cosa:
BALSA n 1
gli altri succedanei
Ciao giobalde

Wood dust from jelutong (Dyera costulata) causes contact allergy [Contact Dermatitis. 1996] - PubMed result

:OT:

Ma quali succedanei... Ti ci metti anche tu? :rolleyes: